A. Donchev, M.C. Galetz, M. Schütze
Materials Science Forum 783-786 (2014), 1117-1122, DOI: 10.4028/www.scientific.net/MSF.783-786.1117
Intermetallic light weight TiAl-alloys are expected to replace the heavy Ni-based super alloys in several high temperature applications. However until now they cannot be used at temperatures above 700°C for longer times due to their insufficient oxidation resistance. The high temperature oxidation behavior can be improved drastically for the use at temperatures up to at least 1050°C by small amounts of fluorine in the surface region of TiAl-components. A thin protective alumina layer is formed after an optimized fluorine treatment during exposure in oxidizing high temperature environments. Results of isothermal and thermocyclic high temperature oxidation tests of untreated and halogen treated TiAl-samples of new types of TiAl-alloys containing Mo, Cu and Si will be presented in this paper. These results will be compared and discussed considering the beneficial effect of fluorine for a later use as e.g. turbine blades in jet engines.